AISI 316L-Ti Stainless Steel Balls

AISI 316Ti Stainless Steel Balls

AISI 316Ti Stainless Steel Balls

These balls are non hardenable austenitic stainless steel with titanium which allow the balls to guarantee a better corrosion resistance in comparison to the AISI 304L & AISI 316L materials. As a standard practice at the Tolia group all stainless steel balls are supplied in a passivated condition.

Applications :
  • Special pumps
  • Ball Valves
  • Food Industry
  • Pharma Industry
  • Cosmetic Industry
Chemical composition
%C %Si %Mn %P %S %Cr %Ni %Mo %N %Ti
0.080 max 0.75 max 2.00 max 0.045 max 0.030 max 16.00-18.00 10.00-14.00 2.00-3.00 0.0100 max 5x%C-0.70
Technical Properties
Property Type U.o.M. Values U.o.M. Values
Hardness Mechanical [HRC] 15 - 35 - -
Ultimate tensile strength Mechanical [MPa] 650 - 1150 [psix10^3] 95 - 166
Size Range/Grade selection
Product Size Range U.o.M. Grade Capabilities
Balls 3.00 mm to 76.20 mm [mm] GR.100 to GR.2000 as per any international standard.

Comparison Chart- Material Corrosion Resistance

Material

 CORROSION RESISTANCE
Air Water Food Liquor Dilute Acid Conc. Acid Chemical
Industrial Atmosphere Salt Air Wet Steam Domestic Water Sea Water Food Product Fruit & Veg. Juice Dairy Product Hot Sulfate Dye HCL H2SO4 HNO3 Phosphoric H2SO4 HNO3 Phosphoric Ammonia Alkaline Salt
AISI-E-52100 3 ← 4 4 ← ← ← ← ← ← ← ← ← ← ← ← ← 2 3
AISI-420 2 4 1 1 ← 3 3 2 ← 3 ← ← ← ← ← ← ← 2 3
AISI 420C 2 4 1 1 ← 3 3 2 ← 3 ← ← ← ← ← ← ← 2 3
AISI 440C 2 3 2 2 ← 2 2 3 ← 4 ← ← ← ← ← ← ← 3 2
AISI 304/302 2 1 1 1 1 1 2 2 1 4 2 2 2 2 😑 2 2 1 1
AISI 316 2 1 1 1 1 1 1 1 2 4 ← 2 1 2 1 1 1 1 2
AISI 1085 3 ← 4 4 ← ← ← ← ← ← ← ← ← ← ← ← ← 2 3

1=Excellent 2 = Good 3 = Fair 4 = Poor

← Will not withstand corrosion

😑 Varies

* = satisfactory only over 75% concentration