AISI 316 / 316L Stainless Steel Balls
Austenitic stainless steel balls with higher corrosion resistance than the 304L series. As a standard practice at the Tolia group all stainless steel balls are supplied in a passivated condition. The high corrosion resistance makes this the perfect ball for the pharma and cosmetic industry.
AISI 316 / 316L Stainless Steel Balls, Austenitic Stainless Steel Balls
Applications :
- Aerosol pumps (medical/pharmaceutical industries)
- Grinding media
- Food Industry
- Bearings
- Agricultural Industry
- Automotive Industry
Chemical composition
| Type | %C | %Si | %Mn | %P | %S | %Cr | %Ni | %N | %Mo |
| 316 | 0.080 max | 1.00 max | 2.00 max | 0.045 max | 0.030 max | 16.00-18.00 | 10.00-14.00 | - | 2.0- 3.0% |
| 316L | 0.030 max | 1.00 max | 2.00 max | 0.045 max | 0.030 max | 16.00-18.00 | 10.00-14.00 | - | 2.0- 3.0% |
International Standards and material codes
| USA | GER | FRA | UK | RUS | CHN | JAP |
| 316 | 1.4401 | Z6CND17.11 | 316S16 | 08KH16N11M3 | 0Cr17Ni12Mo2 | SUS316 |
| 316L | 1.4404 | Z3CND17-11-02 | 316S11 | 03KH17N14M2 | 0Cr19Ni12Mo2 | SUS316L |
Technical Properties
| Property | Type | U.o.M. | Values | U.o.M. | Values |
| Hardness | Mechanical | [HRC] | 10 - 25 (1)* | [HRC] | 25 - 39 (2)* |
| Ultimate tensile strength | Mechanical | [MPa] | 550 - 1250 | [psix10^3] | 80 - 180 |
Note
| Property | Description |
| Hardness* | Balls can be supplied in the ANNEALED (Non Magnetic) condition (HRC 10-25) or COLD WORKED (Magnetic) condition (HRC 25-39). |
Size Range/Grade selection
| Product | Size Range | U.o.M. | Grade Capabilities |
| Balls | 3.00 mm to 76.20 mm | [mm] | GR.40 to GR.2000 as per any international standard. |
| Comparison Chart- Material Corrosion Resistance | |||||||||||||||||||
Material |
CORROSION RESISTANCE | ||||||||||||||||||
| Air | Water | Food | Liquor | Dilute Acid | Conc. Acid | Chemical | |||||||||||||
| Industrial Atmosphere | Salt Air | Wet Steam | Domestic Water | Sea Water | Food Product | Fruit & Veg. Juice | Dairy Product | Hot Sulfate | Dye | HCL | H2SO4 | HNO3 | Phosphoric | H2SO4 | HNO3 | Phosphoric | Ammonia | Alkaline Salt | |
| AISI-E-52100 | 3 | ← | 4 | 4 | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | 2 | 3 |
| AISI-420 | 2 | 4 | 1 | 1 | ← | 3 | 3 | 2 | ← | 3 | ← | ← | ← | ← | ← | ← | ← | 2 | 3 |
| AISI 420C | 2 | 4 | 1 | 1 | ← | 3 | 3 | 2 | ← | 3 | ← | ← | ← | ← | ← | ← | ← | 2 | 3 |
| AISI 440C | 2 | 3 | 2 | 2 | ← | 2 | 2 | 3 | ← | 4 | ← | ← | ← | ← | ← | ← | ← | 3 | 2 |
| AISI 304/302 | 2 | 1 | 1 | 1 | 1 | 1 | 2 | 2 | 1 | 4 | 2 | 2 | 2 | 2 | ← | 2 | 2 | 1 | 1 |
| AISI 316 | 2 | 1 | 1 | 1 | 1 | 1 | 1 | 1 | 2 | 4 | ← | 2 | 1 | 2 | 1 | 1 | 1 | 1 | 2 |
| AISI 1085 | 3 | ← | 4 | 4 | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | ← | 2 | 3 |
1=Excellent 2 = Good 3 = Fair 4 = Poor
← Will not withstand corrosion
😑 Varies
* = satisfactory only over 75% concentration
-